Pengaruh Variasi Sudut Kampuh dan Kuat Arus Pengelasan Hasil Las SMAW Baja SS400 untuk Bahan Bejana Tekan terhadap Kekuatan Tarik dan Kekerasan

Hanan Setia Abadi; Subagiyo Subagiyo

doi:10.61132/venus.v2i5.588

Authors

Hanan Setia Abadi Politeknik Negeri Malang
Subagiyo Subagiyo Politeknik Negeri Malang

DOI:

https://doi.org/10.61132/venus.v2i5.588

Keywords:

current strength, included angle, hardness, tensile strength

Abstract

A pressure vessel is a closed container that stores pressurized liquids or gases. Low-carbon steel is used as a material for pressure vessels that operate at low to moderate temperatures. One of the important aspects of manufacturing pressure vessels is the welding process. The welded area tends to be the weakest point due to exposure to high heat, which can lead to greater residual stress and potentially cause cracking. This study aims to evaluate the effect of variation in ample angle and current strength on mechanical properties, especially tensile strength, and hardness, to determine the optimal amplitude angle and current strength. The research method applied is an experiment by conducting SMAW welding on SS400 steel using E7016 electrodes, with a single V ample angle variation of 55°, 60°, 65°, and strong welding current of 110 A, 120 A, and 130 A, then a tensile test and hardness test are carried out. The results show that the tensile strength of the raw material is 481.2 with a hardness of 191.95 HVN. For the variation of the amputation angle, the highest tensile strength value was recorded at an angle of 55°, which was 567.471 N/mm² , while the lowest was at an angle of 65°, which was 559.997 N/mm² . The highest hardness value at a 65° angle reached 328.422 HVN, while the lowest at a 55° angle was 312.878 HVN. In terms of current strength variation, the highest tensile strength is obtained at 130 A which is 568.421 N/mm² and the lowest at 110 A is 552.339 N/mm² . The highest hardness value is found at a current strength of 110 A, which is 343.411 HVN, and the lowest at a current strength of 130 A, which is 295.122 HVN. The optimal parameters were found at a yield angle of 55° with a tensile strength of 567.471 N/mm² and a hardness of 312.8 HVN and a current strength of 130 A with a tensile strength of 568.421 N/mm² and a hardness of 295.1 HVN.

References

Bin Afan, M., Purwantono, Mulianti, & Rahim, B. (2020). Pengaruh Suhu Penyimpanan Elektroda Low Hydrogen E7016 terhadap Hasil Uji Tekuk Sambungan Las Pelat Baja Karbon SS400. In Jurnal Rekayasa Mesin (Vol. 15, Issue 1). https://jurnal.polines.ac.id/index.php/rekayasa

Dewangga, D. V., & Yulianto, T. (2012). Analisa pengaruh flange angle, toe radius, dan preparation angle terhadap deformasi dan tegangan sisa pada pengelasan butt joint dengan kampuh double v ganda menggunakan metode elemen hingga. Jurnal Teknik ITS, 1(1), G40–G45.

Faizal, M., & Umam, S. (2018). Analisis Kekuatan Dan Kualitas Sambungan Las Dengan Variasi Pendinginan Oli Dan Udara Pada Material Astm a36 Dengan Pengujian Ndt (Non Destructive Test). Bina Teknika, 14(2), 131–138.

Helanianto, H., Epriyandi, E., & Rahmadi, H. (2020). Pengaruh Variasi Arus Pengelasan SMAW Terhadap Kekerasan Logam Induk Dan Logam Las. Elemen: Jurnal Teknik Mesin, 7(2), 138–147.

Huda, M., & Setiawan, F. (2016). Pengaruh variasi sudut kampuh V dan kuat arus dengan las shielded metal arc welding (SMAW) pada baja A36 terhadap sifat mekanik.

Julianti, N. K., Wardani, T. K., Gunardi, I., & Roesyad, A. (2014). Pembuatan Biodiesel dari Minyak Kelapa Sawit RBD dengan Menggunakan Katalis Berpromotor Ganda Berpenyangga γ-Alumina (CaO/MgO/γ-Al2O3) dalam Reaktor Fluidized Bed. Jurnal Teknik ITS, 3(2), B143–B148.

Las, S. (2020). Pengaruh Kuat Arus Dan Besar Sudut Kampuh Terhadap Kekuatan Impact Dan Nilai Kekerasan Plat Baja Karbon Rendah Dengan Menggunakan.

Mudrikunni’am Zumrotul Muniroh, M. (2023). ANALISIS BAJA SS400 HASIL PENGELASAN SMAW DENGAN VARIASI KUAT ARUS TERHADAP NILAI KEKERASAN. SENASTER" Seminar Nasional Riset Teknologi Terapan", 4(1).

Nitiswati, S., & Haryanto, M. (2017). PRE-SERVICE INSPECTION BEJANA TEKAN PEMBANGKIT LISTRIK TENAGA NUKLIR. SIGMA EPSILON-Buletin Ilmiah Teknologi Keselamatan Reaktor Nuklir, 20(2).

Nugroho, A. W., Hartanto, S., Nugroho, M. A. E., & Himarosa, R. A. (2022). Pengaruh Sudut Kampuh V Tunggal terhadap Sifat Mekanis Sambungan Las SMAW pada Pipa Baja Karbon API 5L X46. Semesta Teknika, 25(2), 188–200.

Prastiwi, A. R., & Irfa’i, M. A. (2019). Analisa pengaruh variasi ketebalan plat terhadap kekuatan tarik pada sambungan las butt joint mild steel ss 400. Jurnal Pendidikan Teknik Mesin, 8(3), 37–44.

Rahman Hakim, A., & Imran. (2020). Analisa pengaruh variasi kampuh terhadap hasil pengelasan SMAW pada stainless steel 304 menggunakan pengujian ultrasonic dan kekuatan tarik. Jurnal Polimesin, 18(1), 30–38.

Rahman, H. K., & Sunyoto, S. (2021). Pengaruh Arus SMAW Terhadap Kekuatan Tarik dan Impak Baja Konstruksi IWF JIS G3101 SS400. Jurnal Dinamika Vokasional Teknik Mesin, 6(1), 35–45.

Rauf, F. A., Sappu, F. P., & Lakat, A. M. A. (2018). Uji Kekerasan dengan Menggunaan Alat Microhardness Vickers pada Berbagai Jenis Material Teknik. Jurnal Tekno Mesin, 5(1).

Rodiawati, M., Risano, A. Y. E., & Su’udi, A. (2013). Perancangan Bejana Tekan (Pressure Vessel) untuk Pengolahan Limbah Kelapa Sawit dengan Variabel Kapasitas Produksi 10.000 Ton/Bulan. Jurnal Ilmiah Teknik Mesin, 1(4).

Santoso, T. B., Solichin, S., & Trihutomo, P. (2016). Pengaruh kuat arus listrik pengelasan terhadap kekuatan tarik dan struktur mikro las SMAW dengan elektroda E7016. Jurnal Teknik Mesin, 23(1).

Subagiyo, S., Hadi, S., Agustriyana, L., & Rarindo, H. (2019). ANALISIS KEKUATAN TARIK DAN KEKERASAN BAJA TAHAN KARAT MARTENSITIK HASIL PENGELASAN DENGAN VARIASI LAJU PENDINGINAN. Jurnal Teknologi, 13(2), 1–5.