Pengaruh Panjang  Serat Tandan Kosong Kelapa Sawit pada Pembuatan Palmfiber Reinforced Concrete terhadap Uji Lentur dan Struktur Makro

Vedrix Vantri; Asfarizal Asfarizal

doi:10.61132/venus.v3i2.801

Authors

Vedrix Vantri Institut Teknologi Padang
Asfarizal Asfarizal Institut Teknologi Padang

DOI:

https://doi.org/10.61132/venus.v3i2.801

Keywords:

EFB, Flexural Test, Fiber Length, Macrostructure, PRC

Abstract

This study aims to examine the effect of varying the length of oil palm empty fruit bunch (EFB) fibers on the mechanical properties and macrostructure of Palmfiber Reinforced Concrete (PRC) as an alternative to Glassfiber Reinforced Concrete (GRC). EFB fibers were selected due to their abundance, eco-friendliness, and potential to enhance the mechanical properties of lightweight concrete. The methods employed include flexural testing and macrostructural observation using five fiber length variations (3 cm, 4 cm, 5 cm, 6 cm, and 7 cm). The results show that a fiber length of 5 cm produced the highest flexural stress of 11.78 kg/cm², while a length of 4 cm yielded the highest modulus of elasticity at 162.2 kg/cm². Macrostructural observations revealed good bonding between fibers and matrix in most specimens, although performance differences were observed due to fiber distribution and manual compaction processes. In conclusion, fiber length affects the mechanical performance of PRC, yet production process optimization is necessary to achieve more consistent results.

References

Agustina, L., Udiantoro, & Halim, A. (2016). Karakteristik serat tandan kosong kelapa sawit (TKKS) dengan empty fruit bunches (EFB) fiber with boiling and steaming treatment. Ziraa’Ah, 41(1), 97–102.

Alfianti, J., & Wardhono, A. (2021). Penggunaan serat ampas tebu sebagai bahan pengganti serat fiberglass pada pembuatan campuran plafon GRC terhadap uji kuat lentur, uji kuat tekan, dan uji resapan air. Jurnal Teknik Sipil, 2013–2015.

Anugrah, F., & Mahyudin, A. (2022). Pengaruh komposisi serat sabut kelapa dan pinang terhadap sifat fisik dan mekanik papan beton ringan dengan fly ash sebagai filler. Jurnal Teknik Sipil, 11(1), 8–14.

Aritonang, F. P. (2017). Karakteristik komposit berpenguat serat. Jurnal Teknik Mesin, 3.

Asmeati, Ali, M. Y., Purnama, I., & Paloboran, M. (2016). Analisis uji mekanik dan struktur makro dan mikro terhadap material komposit dengan arah acak serat ampas tebu. Media Komunikasi Pendidikan Teknologi dan Kejuruan, 91–102.

Boimau, K. (2022). Efek panjang serat terhadap sifat tarik komposit poliester berpenguat serat buah lontar yang diberi perlakuan alkali. Jurnal Mesin Nusantara, 5(1), 129–140. https://doi.org/10.29407/jmn.v5i1.17948

Fatmi, R., & Mahyudin, A. (2017). Pengaruh persentase serat sabut kelapa dan foam agent terhadap sifat fisik dan mekanik papan beton. Jurnal Teknik Sipil, 6(4), 324–330.

Ichsan, R. M., Sukma, H., Tatak, A. R., & Tim Mesin Universitas Pancasila. (2020). Pengembangan komposit matriks polimer berpenguat serat tandan kosong kelapa sawit. JMTM, 15, 21–26.

Jati, A. S., Prawatya, Y. E., & Wicaksono, R. A. (2021). Karakterisasi pengaruh orientasi serat terhadap sifat fisis komposit serat tandan kosong kelapa sawit dengan perlakuan alkali (NaOH). Jurnal Teknik Mesin, 2(1), 6–12.

Lusiani, R., Sunardi, & Ardiansah, Y. (2015). 520-1030-1-Sm. Jurnal Ilmiah Teknik Mesin, 1(April), 46–54.

Purboputro, P. I. (2017). Pengaruh panjang serat terhadap kekuatan impak komposit enceng gondok dengan matriks poliester. Media Mesin: Majalah Teknik Mesin, 7(2), 70–76. https://doi.org/10.23917/mesin.v7i2.3088

Ridho, R., Mahyudin, A., & Tim Material Fisika FMIPA Universitas Andalas. (2022). Pengaruh persentase serat plastik terhadap sifat fisis dan mekanis papan beton ringan. Jurnal Teknik Sipil, 11(1), 97–103.

Sunardi, Fawaid, M., & Chumaidi, M. (2016). Pemanfaatan serat tandan kosong kelapa sawit sebagai penguat papan partikel dengan variasi fraksi volume serat. Jurnal Teknik Mesin, 2(1), 36–39.

Susilowati, A., & Rizal, R. S. (2022). Variasi serat gelas pada papan semen. Jurnal Teknik Sipil, 8(2), 339–346.

Tarkono, & Ali, H. (2017). Penambahan serat tandan kosong kelapa sawit (TKKS) dalam rangka mereduksi berat komposit papan semen. Rotor, 10(2), 36. https://doi.org/10.19184/rotor.v10i2.5761

Tri, R., Simatupang, H., & Fitri, M. (2018). Pengaruh ukuran serat ijuk pada material komposit matriks polimer terhadap kekuatan tariknya. Jurnal Teknik Mesin, 9(1).

Yunita, D., & Mahyudin, A. (2017). Pengaruh persentase serat bambu terhadap sifat fisik dan mekanik papan beton ringan. Jurnal Teknik Sipil, 6(4), 348–354.

Zakki, A. F., Fianca, D., & Manik, P. (2014). Studi eksperimen material GRC (glassfiber reinforced concrete) sebagai bahan dasar pada modular floating pontoon. Jurnal Teknik Perkapalan, 20(4), 557–567.