Prilaku Kuat Tekan Beton Self Compacting Concrete Menggunakan Additive Sika Fume
DOI:
https://doi.org/10.61132/konstruksi.v2i2.257Keywords:
Concrete, Sika Fume, Self Compacting Concrete, Compressive StrengthAbstract
This research aims to determine the effect of adding the additive Sika Fume on the compressive strength of concrete. This research uses a type of quantitative research with experimental methods, namely by carrying out several tests on test objects in the laboratory. The results of this research show that the compressive strength of concrete with the addition of sika fume varies 0%, 3%, 5%, 7% and 8% of the cement weight, so the experimental results show that the average compressive strength at the age of 28 days of concrete has a variation of 0 % of 26.14 Mpa, 3% variation of 25.01 Mpa, 5% variation of 27.08 Mpa, 7% variation of 24.16 Mpa, 8% variation of 23.40 Mpa. The concrete compressive strength variation of 5% with an average of 27.08 Mpa is the variation with the highest compressive strength value and reaches the design compressive strength. Meanwhile, a variation of 8% with an average of 23.40 Mpa is the lowest compressive strength value and does not reach the design compressive strength.
References
Hapsari, S. P., Wibowo., Safitri, E. (2017). Kajian Pengaruh Variasi Komposisi Silica Fume Terhadap Parameter Beton Memadat Mandiri Dengan Kuat Tekan Beton Mutu Tinggi. Matriks Teknik Sipil. 1449-1456.
Kushendrahayu, K., Basuki, A., Purwanto, E. (2015). Nilai Kuat Tekan, Kuat Tarik Belah, Dan Kuat Lentur Pada Beton Beragregat Kasar Pet Dengan Penambahan Silica Fume Dan Serat Baja Sebagai Bahan Panel Dinding. E-Jurnal Matriks Teknik Sipil. 688-694.
Mulyono, T. (2003). Teknologi Beton. Yogyakarta: Andi.
Mulyono, T. (2015). Teknologi Beton: Dari Teori Ke Praktek. Universitas Negeri Jakarta: Lembaga Pengembangan Pendidikan.
Nursandah, A., Utomo, S., Hutama, D. A. (2018). Pengaruh Penambahan Bahan Admixture Consol SG Terhadap Kuat Tekan Beton. Agregat. 3(1): 175-181.
Pratama, D., Astuti, R. F., Rochadi, M. T., Kusdiyono. (2018). Kajian Eksperimen Pengaruh Penambahan Silica Fume Terhadap Adhesif Untuk Perbaikan Keramik Dinding. Wahana Teknik Sipil. 23(1): 1-10.
Pratama, E., Hisyam, E. S. (2016). Kajian Kuat Tekan Dan Kuat Tarik Belah Beton Kertas (Papercrete) Dengan Bahan Tambah Serat Nylon. Jurnal Fropil. 4(1): 28-38.
Rahady, M. A., Teguh, M. (2017). Pengaruh Penambahan Silica Fume Dan Superplasticizer Pada Self Compacting Concrete (SCC). Prosiding Kolokium Program Studi Teknik Sipil (KPSTS). Diselenggarakan oleh Program Studi Teknik Sipil Universitas Islam Indonesia: Yogyakarta.
Rahmat., Hendriyani, I., Anwar, M. S. (2016). Analisis Kuat Tekan Beton Dengan Bahan Tambah Reduced Water Dan Accelerated Admixture. Info Teknik. 17(2): 205-218.
Simatupang, P. H., Nasjono, J. K., Mite, K. G. (2017). Pengaruh Penambahan Silica Fume Terhadap Kuat Tekan Reactive Powder Concrete. Jurnal Teknik Sipil. 6(2): 219-230.
SNI 03-1968-1990. Metode Pengujian Analisis Saringan Agregat Halus Dan Kasar. Badan Standarisasi Nasional.
SNI 03-1970-1990. Metode Pengujian Berat Jenis Dan Penyerapan Air Agregat Halus. Badan Standarisasi Nasional
SNI 03-1971-1990. Metode Pengujian Kadar Air Agregat. Badan Standarisasi Nasional
SNI 03-2816-1992. Metode Pengujian Kotoran Organik Dalam Pasir Campuran Mortar atau Beton. Badan Standarisasi Nasional.
SNI 03-2834-2000. Tata Cara Pembuatan Rencana Campuran Beton Normal. Badan Standardisasi Nasional.
SNI 03-4142-1996. Metode Pengujian Jumlah Bahan Dalam Agregat Yang Lolos Saringan No. 200 (0,075 MM). Badan Standarisasi Nasional.
SNI 03-4804-1998. Metode Pengujian Berat Isi Dan Rongga Udara Dalam Agregat. Badan Standarisasi Nasional.
SNI 03-6826-2002. Metode Pengujian Konsistensi Normal Semen Portland Dengan Alat Vicat Untuk Pekerjaan Sipil. Badan Standarisasi Nasional.
SNI 03-6827-2002. Metode Pengujian Waktu Ikat Awal Semen Portland Dengan Menggunakan Alat Vicat Untuk Pekerjaan Sipil. Badan Standarisasi Nasional.
SNI-2417:2008. Cara Uji Keausan Agregat Dengan Mesin Abrasi Los Angeles. Badan Standarisasi Nasional.
Tjokrodimuljo. & Kardiyono. (2007). Teknologi Beton. Yogyakarta: KMTS FT UGM.
Wicaksono, W. S., Wibowo., Safitri, E. (2018). Pengaruh Kadar Silica Fume Terhadap Kuat Tekan Pada High Strength Self Compacting Concrete (HSSCC) Benda Uji Silinder D 7,5 cm x 15cm Usia 14 Dan Hari. E-Jurnal Matriks Teknik Sipil. 638-645.
Zamroni., Susanti, E., Kamarul, D. (2020). Pengaruh Penggunaan Zat Aditif Tipe C Pada Kekuatan Tekan Beton . Jurnal Teknik Sipil. 1(1): 1-10.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2024 Konstruksi: Publikasi Ilmu Teknik, Perencanaan Tata Ruang dan Teknik Sipil
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.